Service HotlineThe material of the combination screw is divided into iron and stainless steel. The iron ones are made of different iron screw wires. Generally, the wire of the combination screw is 1010, 1018, 10B21 and so on. 10B21 is used to make 8.8 grade combination screws. Like 8.8 grade hexagon socket head combination screws, 10B21 wire is often used. When done, go to heat treatment. After heat treatment, remove hydrogen and electroplating. This is to prevent the spring washer of the socket head cap screw from breaking. Stainless steel combination screws, in the combination screw market, generally refer to stainless steel SUS304 combination screws. 201 combination screws generally do very little. Few combination screw manufacturers produce 201 combination screws. Because the hardness of the screw wire of stainless steel 201 is not well controlled, it is easy to produce cracks.
Standards are norms, and each country and sector has its own standards. The most commonly used standards in our daily business are as follows: GB—China National Standard (National Standard) ANSI—American National Standard (American Standard) DIN—German National Standard (German Standard) ASME—American Society of Mechanical Engineers Standard JIS - Japanese National Standard (Japanese Standard) BSW - British National Standard GB - National Standard is one of many standards in my country, as well as industry standards, professional standards and department standards. National standards are divided into: GB (mandatory standards) and GB/T (recommended standards) and GBn (national internal standards) and so on. We usually see GB30, GB5783, etc. are mandatory standards. In addition to some basic dimensions such as head-to-side, head thickness, etc., the above standards are mainly different in the threaded part. The threads of GB, DIN, JIS, etc. are all in MM (millimeters), which are collectively referred to as metric threads. Another thread like ANSI, ASME, etc. is called American standard thread in inches. In addition to metric threads and American threads, there is also a BSW-imperial standard, whose threads are also in inches, commonly known as Wyeth threads.
When the countersunk head screws and hexagon socket head bolts are produced by the cold heading process, the original structure of the steel will directly affect the forming ability of the cold heading process. In the process of cold heading, the plastic deformation of the local area can reach 60%-80%, so the steel must have good plasticity. When the chemical composition of the steel is constant, the metallographic structure is the key factor to determine the plasticity. It is generally believed that the coarse flaky pearlite is not conducive to cold heading forming, while the fine spherical pearlite can significantly improve the plastic deformation ability of the steel. For medium carbon steel and medium carbon alloy steel with a large amount of high-strength bolts, spheroidizing (softening) annealing is performed before cold heading, so as to obtain uniform and fine spheroidized pearlite to better meet the actual production needs. For the softening annealing of medium carbon steel wire rods, the heating temperature should be kept above and below the critical point of the steel, and the heating temperature should not be too high, otherwise tertiary cementite will precipitate along the grain boundary, resulting in cold heading cracking. The wire rod of medium carbon alloy steel is annealed by isothermal spheroidization. After heating at AC1+ (20-30%), the furnace is cooled to slightly lower than Ar1, the temperature is about 700 degrees Celsius for an isothermal period, and then the furnace is cooled to about 500 degrees Celsius and air-cooled. The metallographic structure of the steel changes from coarse to fine, from flake to spherical, and the cracking rate of cold heading will be greatly reduced. The general area of softening annealing temperature for 35\45\ML35\SWRCH35K steel is 715-735 degrees Celsius; while the general heating temperature for spheroidizing annealing of SCM435\40Cr\SCR435 steel is 740-770 degrees Celsius, and the isothermal temperature is 680-700 degrees Celsius.
There is an anti-theft screw, which can prevent the use of any disassembly tool for disassembly, and effectively plays the role of anti-theft. Its structure is that the anti-theft screw is composed of two parts; the upper part is a hexagonal part, and the lower part is a threaded part; the hexagonal part and the threaded part are connected in rotation; The core shell is formed with the lock core; the lock core is rotatably connected with the lock core shell. The shell of the lock cylinder is fixedly connected with the hexagonal piece, and the starting structure is as follows: a pin hole is arranged on the hexagonal piece; The lower part of the hexagonal part is provided with a polygonal hole, which is connected with the polygonal hole on the threaded part; the lower part of the lock cylinder is a threaded rod; the threaded rod is located in the polygonal hole; The edge block moves up and down in the polygonal hole. When working, slowly twist the hexagonal piece from left to right and turn the key at the same time to achieve the alignment of the upper and lower polygonal holes.
The grooved embedded parts are usually connected by bolts, and there are many types of T-bolts used with the grooved embedded parts. position, so that the T-bolt can form a stable connection with the groove-type embedded part, but in the actual installation process, the T-bolt pressed into the groove-type embedded part is prone to loosening problems, so it is difficult to better Fixed in trough embedded parts.
We have many years of experience in the production and sales of screws, nuts, flat washers, etc. The main products are: black high-strength hexagon nuts, galvanized gasket manufacturers, copper rivets, galvanized screws and other products, we can provide you with suitable fasteners. Firmware Solutions.