Service HotlinePins are widely used. In the connection of the rotating mechanism of two moving components, such as the crank mechanism, the turning mechanism, the connection between the hydraulic cylinder and the moving parts, the pins are used. kind. In order to ensure the normal use of the running equipment and prevent the cylindrical pin from slipping out and falling off during use, some anti-falling methods are usually used at the head of the pin, such as 1. Drill holes and insert cotter pins to prevent the pins from slipping out; 2. The external thread is tightened with a nut to prevent the pin from slipping out; 3. The slot is clamped with a circlip to prevent it from slipping out, etc. These measures make the cylindrical pin very practical in the case of infrequent disassembly and assembly, but in the actual use of the field, in order to prevent the collision of some equipment during each troubleshooting or maintenance, the pin needs to be pulled out and turned up, etc. After the failure or maintenance is completed, put down and then insert the pin to restore, this process will bring trouble to the actual operator. For example, special tools must be brought with you every time you disassemble and assemble the pin, and the split pin or the circlip is easily damaged after repeated disassembly and assembly. , In order to save trouble, the operator sometimes uses iron wire to thread or fasten it instead, and even does not remove the pin for the sake of speed and convenience, which is easy to cause damage to the equipment when dealing with faults.
(1) The screw-in performance test is to screw the self-tapping locking screw sample into the test plate until one complete thread completely passes the test without breaking. (2) The destructive torque test is to clamp the stem of the self-tapping locking screw specimen in a thread mold or other device that matches the screw thread, and uses a calibrated torque-measuring device to measure the screw. Torque is applied until fracture, which should not occur in the clamped threaded portion. (3) Carry out a tensile test on the screw sample to check the minimum tensile load for failure. The fracture should be within the length of the rod or the unthreaded thread, and should not occur at the junction of the nail head and the rod. Before the sample breaks, it should be It can reach the minimum tensile load specified by the corresponding performance class. (4) Hydrogen embrittlement is a problem that must be strictly paid attention to in the surface treatment process of self-tapping locking screws. In the pickling process, the screw is stirred in dilute hydrochloric acid, and the amount of hydrogen absorbed by the pickling steel increases linearly with the square root of time and reaches the saturation value. Less than 100%, a large number of hydrogen atoms will be produced, which will be attached to the surface of the screw, resulting in hydrogen infiltration, and the steel will become brittle due to the absorption of hydrogen. The self-tapping locking screw takes 6~8h to drive hydrogen, and the temperature is 160~200℃ (phosphating) and 200~240℃ (electroplating). However, in the production process, the hydrogen drive time should be determined according to many production conditions such as core hardness, surface roughness, electroplating time, coating thickness, pickling time, and acid concentration. It is best to do it before passivation and just after electroplating.
At present, with the development of the manufacturing industry, many parts with strange shapes are widely used in aviation, aerospace and other industrial fields, one of which is an L-shaped cylindrical pin. The upper end is provided with a 2.55×4.95 U-shaped boss. The parallelism error between the upper end face and the lower end face of the boss is required to be less than 0.01 mm. The L-shaped cylindrical pin requires high machining accuracy and is difficult to clamp on the machine tool. It is difficult to process. When the forming part is cut off, the cut surface, that is, the upper end surface of the boss, will leave a small column platform. When processing this end surface, in the prior art, a vise is generally used to process such an L-shaped cylindrical pin. Or copper sleeves are clamped, and then processed; however, due to the small size of the parts, the L-shaped cylindrical pin workpiece is difficult to clamp; due to the high precision required for each machined surface of the workpiece, when clamping with a vise , the clamping force of the vise is difficult to control, and it is easy to crush and scratch the surface of the workpiece; and when using a vise or a copper set clamp, only one workpiece can be clamped for each processing and production, and it is difficult to ensure the upper and lower planes of the parts after the clamping is completed. Parallelism machining error, resulting in low parts processing quality and low production efficiency.
Heat resistance refers to both the oxidation resistance or gas medium corrosion resistance at high temperature, that is, thermal stability, and at the same time, it has sufficient strength at high temperature, that is, thermal strength. As the material requirements of products produced by customers are getting higher and higher, the requirements for screws used in product materials are also getting higher and higher. When product materials face harsh environments and special occasions, more and more high-quality mechanical properties of stainless steel screws are used. Therefore, stainless steel screws were selected. The requirements are getting higher and higher, and the material of stainless steel screws is getting higher and higher. Therefore, many ordinary stainless steel screws SUS201 are replaced by stainless steel SUS304 screws and stainless steel screws SUS316. Of course, if some requirements are not so high, general customers will choose stainless steel screws SUS201, which are relatively cheap in cost.
The rubber ring and the metal ring are integrally bonded and vulcanized. It is a sealing ring used to seal the thread and flange connection. The ring includes a metal ring and a rubber gasket. The metal ring is rust-proof, and the rubber ring is generally made of oil-resistant nitrile rubber or fluororubber. Combination pads are available in metric and inch sizes, and the standard JB982-77 specifies the combination of metal pads and rubber. Combination sealing washer is used for threaded pipe joints and screw plug sealing. It is generally used with ferrule type pipe joints to block oil ports. It is mainly used for end face static sealing of threaded joints of hydraulic valve pipe joints. It is suitable for British and American standards. Inch thread and end face static seal at French and German standard metric thread connections, etc. The combined sealing gasket can be divided into A type and B type according to the structure; it can be divided into full package and half package according to the difference of rubber.
We have many years of experience in the production and sales of screws, nuts, flat washers, etc. The main products are: DIN7, color zinc hexagon nuts, copper nuts, hexagon socket flat cups and round cups and other products, we can provide you with suitable fasteners for you solution.