Service HotlineReference standard GB 90 Fastener acceptance inspection, marking and packaging GB 196 Basic dimensions of ordinary threads (1～600mm in diameter) GB 197 Tolerance and fit of ordinary threads (1～355mm in diameter) GB 230 Test method for Rockwell hardness of metals GB 699 High-quality carbon Plain structural steel technical conditions GB 1237 Marking method of fasteners GB 5267 Electroplating layer of threaded fasteners GB6394 Determination of average grain size of metals
In order to meet the requirements of anti-loosening bolts of parts with small surface hardness such as plastic parts, Yueluo provides a spring washer and the installation structure of the spring washer, which can effectively reduce the damage of the spring washer to the surface of the parts. And meet the anti-loosening effect of the spring washer. The technical solution provided by Yueluo is a spring washer, which includes a washer body with at least two raised claws on the washer body
Usually, the forming of the bolt head adopts cold heading plastic processing. Compared with the cutting process, the metal fiber (metal wire) is continuous along the shape of the product, and there is no cut in the middle, thus improving the strength of the product, especially the mechanical properties. The cold heading forming process includes cutting and forming, single-station single-click, double-click cold heading and multi-station automatic cold heading. An automatic cold heading machine performs multi-station processes such as stamping, heading forging, extrusion and diameter reduction in several forming dies. The processing characteristics of the original blank used by the single-station or multi-station automatic cold heading machine are determined by the size of the bar with a length of 5-6 meters or the wire rod with a weight of 1900-2000KG, that is, the characteristics of the processing technology. The point is that cold heading does not use pre-cut single blanks, but uses the automatic cold heading machine itself to cut and upset (if necessary) blanks from bars and wire rods. Before extruding the cavity, the blank must be shaped. A blank that meets the technological requirements can be obtained by shaping. Before upsetting, reducing and positive extrusion, the blank does not need to be shaped. After the blank is cut, it is sent to the upsetting and shaping station. This station can improve the quality of the blank, reduce the forming force of the next station by 15-17%, and prolong the life of the die, and the bolts can be made with multiple diameter reductions. The precision that can be achieved by cold heading is also related to the selection of the forming method and the procedure used. In addition, it also depends on the structural characteristics of the equipment used, the process characteristics and its state, the precision of the tool and die, the life and the degree of wear. For high-alloy steel used in cold heading forming and extrusion, the roughness of the working surface of the cemented carbide mold should not be greater than Ra=0.2um. When the roughness of the working surface of this type of mold reaches Ra=0.025-0.050um, it has the highest life.
The material of the round head three combination screw is divided into iron and stainless steel. The iron ones are made of different iron screw wires. Generally, the wire of the combination screw is 1010, 1018, 10B21 and so on. 10B21 is used to make 8.8 grade combination screws. Like 8.8-grade socket head cap screws, 10B21 wires are often used to make them. When done, go to heat treatment. After heat treatment, remove hydrogen and electroplating. This is to prevent the spring washer of the socket head cap screw from breaking. Stainless steel combination screws, in the combination screw market, generally refer to stainless steel SUS304 combination screws. 201 combination screws generally do very little. Few manufacturers of round head three combination screws produce 201 combination screws. Because the hardness of the screw wire of stainless steel 201 is not well controlled, it is easy to produce cracks. Introduction to the basic knowledge of electroplating round head combination screw electroplating generally refers to the de-plating of iron combination screws. Electroplating is divided into environmental protection and non-environmental protection. Commonly used combination screw electroplating colors include green color zinc, green blue zinc, green white zinc, green nickel, red color, white zinc, white nickel, etc. Cross recessed combination screws, hexagon combination bolts and self-tapping combination screws are used in the same way as the corresponding cross recessed screws, hexagon head bolts and self-tapping screws. The main feature of these combination screws is that they are equipped with corresponding washers, which are very convenient to use.
The manual dismantling of the rivets of the automobile frame delays the production cycle of the product and increases various production costs, so a special tooling is desperately needed to meet the actual needs.
We have many years of experience in the production and sales of screws, nuts, flat washers, etc. The main products are: expansion bolt pipes, gypsum board expansion screws, explosion screws, machine tooth flat end screws and other products, we can provide you with suitable fastener solutions for you Program.