Service HotlineThe post-treatment of nickel-phosphorus plating includes two main processes of driving hydrogen and polishing. ①Hydrogen drive; according to the relevant standards, the hydrogen drive temperature after plating is 200±10℃, and the treatment time is 2h. 200 ℃ is beneficial to eliminate hydrogen embrittlement, relax internal stress, improve the bonding force between the coating and the substrate, and improve the corrosion resistance of the coating. ②Polishing; the polished bolt has a bright appearance, but in order to better improve the quality of the coating, smooth the tiny traces, and obtain a bright mirror-like surface, the coating needs to be polished with a polishing machine.
Referring to Figure 1, one end of the existing insert nut 1' is embedded in the injection molded part 2', and the other end is exposed to the injection molded part 2'. The insert nut 1' has opposite lower and upper end surfaces in the axial direction. The end face of one end of the insert injection molded part 2' is the lower end face. In order to reduce the resistance during hot pressing, the connection between the inner wall surface and the lower end surface of the insert nut 1 ′ is provided with an inclined surface. However, when the embedded nut 1' of this structure is hot-pressed, the hot melted glue will generate a shunt that rises along the slope, and then a convex peak is formed in the screw hole of the embedded nut 1', and the convex peak occupies the screw. The space in the hole prevents the screw 5' from being completely screwed in; at the same time, due to the shunting of the hot solder, the knurling of the inner nut 1' near the upper end face cannot be filled with the solder, which makes the inner nut 1' and the inner nut 1' and The injection part 2' is not firmly embedded. Therefore, the locking strength of the existing insert nut 1 ′ and the screw 5 ′ after being hot-pressed is relatively low.
Stud, also known as double-ended screw or double-ended stud. It is used to connect the fixed link function of the machine. The stud bolt has threads at both ends, and the screw in the middle is thick or thin. Generally used in mining machinery, bridges, automobiles, motorcycles, boiler steel structures, pendant towers, long-span steel structures and large buildings.
Building aluminum alloy formwork is a new type of building formwork, which conforms to the four sections and one environmental protection policy. It is economical, fast, high-quality and environmentally friendly. Its application is of great significance to building energy conservation and environmental protection. The aluminum template is filled with aluminum template pins. However, the pins in the prior art have low connection strength during use, which is likely to cause the hole to be repaired weakly.
The tie rod and joint of the high-voltage isolating switch are often connected by driving an elastic cylindrical pin into the connecting pin hole. The traditional assembly method is to prevent the tie rod and joint from the V-block, and hold the elastic cylindrical pin to align the connecting pin hole. Then hit it with a hammer. Since the elastic cylindrical pin is small, it is easy to injure people's hands by adopting this assembly method, and at the same time, the elastic cylindrical pin is not positioned accurately, which causes large assembly errors and low assembly efficiency.
We have many years of experience in the production and sales of screws, nuts, flat washers, etc. The main products are: copper inner teeth plastic handle nuts, GB819 fastening countersunk head bolts, shock-proof opening spring washers, flat gasket specifications and other products, we can provide you with products such as Provide the right fastener solution for you.