Service HotlineStainless steel usually refers to steel that has the ability to resist corrosion by air, water, acid, alkali salt or other medium. Depending on the alloy composition, the focus is on rust resistance and acid resistance. Although some steels are rust-resistant, they are not necessarily acid-resistant, and acid-resistant steels are usually rust-resistant. Austenitic stainless steel is mainly used in the production of fasteners. In people's daily life, the stainless steel often referred to is also austenitic stainless steel. The stainless steel fasteners we use are mainly made of austenitic 302, 304, 316 and low nickel 201 as raw materials.
The retaining ring with an open ring structure is a commonly used mechanical part. It has standardized design standards. Its main function is to fasten the ring-shaped parts on the shaft, which can prevent other parts mounted on the shaft from moving. kinds of fasteners. In the prior art, the retaining ring is mainly processed by stamping, which has the following defects: 1. The material utilization rate is low;
When processing some disc parts, the mandrel is often used for positioning, and the nut is pressed on it. However, the ordinary nut cannot meet the requirements due to its small end face and poor flatness. The user needs to make the nut, and the cost is high due to single-piece production.
In CN203807560, nails and bolts are used to connect the plates, but the heads of the nails and the bolts are enlarged ends that are wider than the rods, and the heads of the nails and the bolts cannot penetrate into the interior of the door body, so in terms of appearance, the more More nails and bolts will leave more spots on the surface of the door that are not suitable for the door itself. In the prior art, the treatment method for these spots is generally to paint with paint, which can only make the door panel consistent with the head of the nail and the bolt in color, but cannot change the shape of the head of the nail and the bolt, and the appearance is still good. Obvious spots were noticed, which made the door panels connected by nails and bolts to the panels, which could not be used as door panels for household doors.
When using screws, if you can understand the mechanical properties of screws first, then you can use screws better. Different types of screws have different mechanical properties, and the different mechanical properties lead to different occasions when screws are used. 1. Self-tapping screws: mechanical performance requirements 1. Heart hardness: standard value HRC28-38. When testing, take the section 1-2 times the diameter of the name from the tail. If the length of the name is too short, it can be embedded first, and then the hardness is measured. 2. Surface hardness: standard MIN HV450. 3. Carburized layer: standard 4#-6#: 0.05-0.18mm, 8#-12#: 0.10-0.23 mm, 14#: 0.13-0.28 mm. The main purpose of carburizing is to enhance the surface hardness and ensure the strength of the teeth. If the decarburization is too deep and the carburization is insufficient, the strength of the teeth will not meet the requirements, that is, the teeth will be damaged during the screw-in test. 4. Torque: standard specification 4#5#6#7#8#10#12#14#A tooth 14212835455696145AB tooth 142128354565102165. 5. Screw-in test: screw the self-tapping screw into a steel plate with a reserved test hole. The self-tapping screw should form a matching thread in the test plate, and the thread of the screw itself will not be deformed or damaged until the end. Tapered threads pass completely through the test plate. The screw-in test is only applicable to AB, B, BP and other types of self-tapping screws. It is stipulated in IFI that the test plate shall be prepared from semi-hard low-carbon cold-rolled steel, and the hardness of the steel plate is 70–85HRB in Rockwell. The standard specification of the steel plate, that is, the thickness, is shown in the table below. The test hole should be punched or drilled, and the tolerance is the specified nominal diameter (see the table below) ± 0.025mm. Specifications 6#7#8#10#12#1/4 Test plate thickness (mm) 1.85-1.953.12-3.234.68-4.84 Aperture (mm) ±0.0252.953.263.454.044.765.50.
We have many years of experience in the production and sales of screws, nuts, flat washers, etc. The main products are: ISO14580 screws, half countersunk head screws, bronze spring washers, hairpin pins and other products, we can provide you with suitable fastener solutions for you Program.