Service HotlineThe assembly of hollow rivets and flat head screws riveted on the cover plate is assembled in the product. Compared with the method of connecting with bolts, the loading and unloading speed can improve the efficiency by about 80% to 90%, and is widely used. The assembly needs to riveted hollow rivets and flat head screws on the cover plate, and ensure that the riveted flat head screws can rotate flexibly. When riveting, it is necessary to use special tools to riveted the hollow rivets, flat head screws and cover plates together for riveting. In the existing riveting process, the oval head screw is often damaged due to the action of external force. The positioning process is cumbersome and the work efficiency is low.
Screws and bolts are common connecting fasteners. The diameter of the thread is as small as less than one millimeter and as large as several hundred millimeters or even larger. The vast majority of threaded connections are pre-tightened during assembly in order to enhance the rigidity, tightness, anti-loosening ability of the connection and prevent the sliding of the bolted connection under lateral load. The pre-tightening force is determined according to the force of the bolt group and the working requirements of the connection. For important threaded connections, the preload must be measured and controlled.
1. For low strength (below 500 N/mm2 or below 60000 psi) bolts use general soft steel, generally use SAE 1008 or JIS SWRM 8 (or SWRCH 8). 2. Lower strength (600 N/mm2 or 74000 psi) ) bolts use general soft steel, but limited carbon content grade, generally use SAE 1010 - 1015 or JIS SWRM 10 - 15 (or SWRCH 10 - 15). .3. Higher strength ( 800 N/mm2 or 125000 psi ) bolts of medium carbon steel, low carbon boron steel plus quenching and tempering, generally use SAE 1035 - 1040 or SWRCH 35K - 40K. 4. High strength (900 N/mm2 or more or 150000 psi or more) bolts use medium carbon Alloy steel or low carbon boron steel, in terms of application, if the metric Class 10.9 uses low carbon boron steel, the imprint should be added under the series imprint to become 10.9, and the imprint of the inch 8.2 grade is also used with the general Grade 8 bolts The imprint is different for easy identification. High-strength bolts made of low carbon boron steel cannot be used in high temperature conditions. The design strength exceeds Class 12.9 or ASTM A574 ultra-high strength bolts are limited to medium carbon alloy steel plus quenching and tempering. The performance grades of bolts for steel structure connection are divided into more than 10 grades such as 3.6, 4.6, 4.8, 5.6, 6.8, 8.8, 9.8, 10.9, 12.9, etc. Among them, the bolts of grade 8.8 and above are made of low-carbon alloy steel or medium-carbon steel and are heat-treated (quenching, tempering), commonly known as high-strength bolts, the rest are commonly known as ordinary bolts. The bolt performance grade label consists of two parts of numbers, which represent the nominal tensile strength value and yield ratio of the bolt material respectively. For example, a bolt with a performance level of 4.6 means: 1. The nominal tensile strength of the bolt material is 400MPa; 2. The yield ratio of the bolt material is 0.6; 3. The nominal yield strength of the bolt material is 400×0.6=240Mpa . Performance level 10.9 high-strength bolts, after heat treatment, can achieve: 1. The nominal tensile strength of the bolt material is 1000MPa; 2. The yield ratio of the bolt material is 0.9; High-strength bolts, processing and manufacturing problems are compared Small, general fastener manufacturing companies can master the manufacturing process; but problems are prone to occur in material selection and heat treatment. Material selection is the primary link. Various alloying elements have a great influence on the properties of the material, and the material must be subjected to spectral composition analysis; secondly, the fracture problem and the choice of heat treatment process have a great influence and are very important. Dealers and traders must control the inspection and performance testing links; automotive fasteners have high requirements and must carefully control the quality.
The purpose of Guangdong Yueluo Hardware Industry Co., Ltd. is to overcome the deficiencies in the existing technology and provide a square nut fastener for cable tray installation, which has a simple and reasonable structure, and is extremely convenient and flexible to operate; it does not occupy C-shaped steel after installation. The space at the bottom increases the diversity of installation, and can be applied to square nuts of different thicknesses, and the installation is firm
High-strength fastener materials mainly include ML35, 35K, ML40Cr, ML35CrMo steel, etc., of which 75ML35CrMo steel is imported. The main problems of the material are box segregation, decarburization, cracks and so on. The material needs to be spheroidized and annealed before cold forming, and the annealing is carried out in an oil furnace. There is no protective atmosphere in the furnace, and there is a decarburization phenomenon. 1.2 The high-strength fasteners, mainly grade 12.9, are quenched and tempered on the chain casting furnace production line. The temperature and atmosphere in the furnace are controlled by computer, and Rx gas is used as a protective atmosphere. Heating and anti-oxidation and decarburization can be effectively controlled, and the quality of the fasteners is intact during the heating process. The high-strength fasteners mainly of grade 8.8 are quenched and tempered on the vibrating hearth furnace. Affected by the structure of the vibrating hearth furnace, the sealing performance of the furnace is poor, the Rx atmosphere is not easy to control, the temperature difference of the furnace is large, and the parts are heated in the furnace. The collision and the length of time are inconsistent, and the quality of the fasteners during the heating process is poor, and there are phenomena such as decarburization, bumps, and uneven heating.
We have many years of experience in the production and sales of screws, nuts, flat washers, etc. The main products are: round head straight thread screws, core pulling aluminum rivets, galvanized hollow rivets, black and red diamond pattern aluminum column connection long nuts and other products, we can provide You have the right fastener solution for you.