Service HotlineWhen checking the finished blind rivet, check: the diameter of the rivet body, the length of the rivet body, the thickness of the rivet body cap, the diameter of the cap, the total length of the mandrel, the exposed size of the mandrel, the size of the nail cap, and the outer diameter after assembly can be considered. In the actual inspection, the weak links of the product can be measured, such as: tensile force, shear resistance, and core pull-out resistance. The key is to pay attention to the rivets, if the rivets are insufficient, whether they are riveted in place; or because the cap of the mandrel is too large, so that the mouth of the rivet body cannot be pulled down; and there are jump heads, that is, the mandrel is too low or broken. The size is too small etc. Length measurement of closed blind rivets
Lock washers feature easy installation. 1. Just place the helical tooth surfaces on the inner side of the two washers against each other and place them between the nut and the connecting material; 2. After the nut is tightened, the radially convex surface on the outer side of the lock washer and the contact surfaces at both ends are in an engaged state, and The angle of the slope angle of the helical tooth surface on the inner side of the washer is greater than the thread angle of the bolt; 3. When the bolt is elongated due to mechanical vibration, the nut will rotate and loosen accordingly. Because the frictional force of the outer radial convex surface of the lock washer is greater than the frictional force between the inner helical tooth surfaces. In this state, only the relative dislocation between the inner helical tooth surfaces is allowed to generate a certain lifting tension; 4. When the bolt shrinks, the helical tooth surface of the washer will make the nut return to its original position. So as to achieve 100% anti-loose and tightening effect; 5. Washers are suitable for relatively flat and smooth surfaces; 6. If the connecting material is non-metallic material, a metal plate can be fixed on the connecting material, so that the Use the lock washer; 7. There is no need to use a torque wrench when installing the lock washer; 8. You can choose to use an air tool when installing or removing the lock washer.
In the existing life, repair parts are often used to repair the cassettes with damaged screw holes, and the screw holes on the repair parts are used instead of the original damaged cassette screw holes. However, in the prior art (application number: 201520948368.5), the restoration is fixed by rotating the support of the restoration, which is often inconvenient due to the small space of the cassette. In addition, the set screw in the prior art mainly fastens the object through the end of the screw without threaded holes, which makes it difficult to install external screws. Based on this, a method of extruding the support through a set screw with screw installation holes and tightening the repair piece, and then installing the screw on the set screw, will facilitate the quick installation and use of the repair piece.
1. For low strength (below 500 N/mm2 or below 60000 psi) bolts use general soft steel, generally use SAE 1008 or JIS SWRM 8 (or SWRCH 8). 2. Lower strength (600 N/mm2 or 74000 psi) ) bolts use general soft steel, but limited carbon content grade, generally use SAE 1010 - 1015 or JIS SWRM 10 - 15 (or SWRCH 10 - 15). .3. Higher strength ( 800 N/mm2 or 125000 psi ) bolts of medium carbon steel, low carbon boron steel plus quenching and tempering, generally use SAE 1035 - 1040 or SWRCH 35K - 40K. 4. High strength (900 N/mm2 or more or 150000 psi or more) bolts use medium carbon Alloy steel or low carbon boron steel, in terms of application, if the metric Class 10.9 uses low carbon boron steel, the imprint should be added under the series imprint to become 10.9, and the imprint of the inch 8.2 grade is also used with the general Grade 8 bolts The imprint is different for easy identification. High-strength bolts made of low carbon boron steel cannot be used in high temperature conditions. The design strength exceeds Class 12.9 or ASTM A574 ultra-high strength bolts are limited to medium carbon alloy steel plus quenching and tempering. The performance grades of bolts for steel structure connection are divided into more than 10 grades such as 3.6, 4.6, 4.8, 5.6, 6.8, 8.8, 9.8, 10.9, 12.9, etc. Among them, the bolts of grade 8.8 and above are made of low-carbon alloy steel or medium-carbon steel and are heat-treated (quenching, tempering), commonly known as high-strength bolts, the rest are commonly known as ordinary bolts. The bolt performance grade label consists of two parts of numbers, which represent the nominal tensile strength value and yield ratio of the bolt material respectively. For example, a bolt with a performance level of 4.6 means: 1. The nominal tensile strength of the bolt material is 400MPa; 2. The yield ratio of the bolt material is 0.6; 3. The nominal yield strength of the bolt material is 400×0.6=240Mpa . Performance level 10.9 high-strength bolts, after heat treatment, can achieve: 1. The nominal tensile strength of the bolt material is 1000MPa; 2. The yield ratio of the bolt material is 0.9; High-strength bolts, processing and manufacturing problems are compared Small, general fastener manufacturing companies can master the manufacturing process; but problems are prone to occur in material selection and heat treatment. Material selection is the primary link. Various alloying elements have a great influence on the properties of the material, and the material must be subjected to spectral composition analysis; secondly, the fracture problem and the choice of heat treatment process have a great influence and are very important. Dealers and traders must control the inspection and performance testing links; automotive fasteners have high requirements and must carefully control the quality.
T-bolts for channel steel usually include a head and a shank. The shank is provided with threads. Traditional T-bolts for channel steel are used for channel steel, and both channel steel and bolts are made of steel. , the two are prone to thermal expansion and contraction due to changes in the external ambient temperature, and are prone to loosening, resulting in unstable connections.
We have many years of experience in the production and sales of screws, nuts, flat washers, etc. The main products are: toothed screws, color zinc plated copper columns, iron color zinc flat head rivet nuts, washers sets and other products, we can provide you with suitable products for you. Fastener Solutions.