Service HotlineThe flat washer is mainly used to reduce the pressure. When some parts are tightened with a large axial force, it is easy to press the washer into a dish shape. At this time, it can be solved by changing the material and increasing the hardness.
GB97.1.CATPart GB97.1.SLDPRT Nominal size d d1 d2 h 1000 weight (kg) ≈ nominal diameter (NND) inner diameter (SD1) outer diameter (SD2) thickness (SD) — 5 5.3 10 1 0.443 Spring washer spring Wasket 6 6.4 12 1.6 1.0518 8.4 16 1.6 1.828 10 10.5 20 2 3.57 14 15 28 2.5 8.611 16 17 30 3 11.29 20 21 37 37.16 24 25 44 4 32.31 30 31 56 4 53.61 36 37 66 5 92.03
A rivet is a nail-shaped object used to connect two parts (or members) with a through hole and a cap on one end. In riveting, the riveted parts are connected by their own deformation or interference. There are many types of rivets, and they are informal.
The main purpose of the embedded nut is to replace the direct opening of screw holes on the injection molded parts, so as to improve the strength of the screw holes of the injection molded parts. Referring to FIG. 1 , in order to lock the workpiece 3 ′ on the injection molded part 2 ′, the screw 5 ′ passes through the through hole on the workpiece 3 ′ and is screwed into the screw hole of the embedded nut 1 ′ to fix the workpiece 3 ′. The embedding between the embedded nut 1' and the injection-molded part 2' generally includes two ways. One is to heat the embedded nut 1' and then insert it into the injection-molded part 2' by hot pressing; the other is to insert the embedded nut into the injection-molded part 2'. 1' and the injection part 2' are integrally injection-molded. In order to ensure the bonding strength between the inner nut 1' and the injection molded part 2', knurling is provided on the outer peripheral surface of the inner nut 1'.
1. For low strength (below 500 N/mm2 or below 60000 psi) bolts use general soft steel, generally use SAE 1008 or JIS SWRM 8 (or SWRCH 8). 2. Lower strength (600 N/mm2 or 74000 psi) ) bolts use general soft steel, but limited carbon content grade, generally use SAE 1010 - 1015 or JIS SWRM 10 - 15 (or SWRCH 10 - 15). .3. Higher strength ( 800 N/mm2 or 125000 psi ) bolts of medium carbon steel, low carbon boron steel plus quenching and tempering, generally use SAE 1035 - 1040 or SWRCH 35K - 40K. 4. High strength (900 N/mm2 or more or 150000 psi or more) bolts use medium carbon Alloy steel or low carbon boron steel, in terms of application, if the metric Class 10.9 uses low carbon boron steel, the imprint should be added under the series imprint to become 10.9, and the imprint of the inch 8.2 grade is also used with the general Grade 8 bolts The imprint is different for easy identification. High-strength bolts made of low carbon boron steel cannot be used in high temperature conditions. The design strength exceeds Class 12.9 or ASTM A574 ultra-high strength bolts are limited to medium carbon alloy steel plus quenching and tempering. The performance grades of bolts for steel structure connection are divided into more than 10 grades such as 3.6, 4.6, 4.8, 5.6, 6.8, 8.8, 9.8, 10.9, 12.9, etc. Among them, the bolts of grade 8.8 and above are made of low-carbon alloy steel or medium-carbon steel and are heat-treated (quenching, tempering), commonly known as high-strength bolts, the rest are commonly known as ordinary bolts. The bolt performance grade label consists of two parts of numbers, which represent the nominal tensile strength value and yield ratio of the bolt material respectively. For example, a bolt with a performance level of 4.6 means: 1. The nominal tensile strength of the bolt material is 400MPa; 2. The yield ratio of the bolt material is 0.6; 3. The nominal yield strength of the bolt material is 400×0.6=240Mpa . Performance level 10.9 high-strength bolts, after heat treatment, can achieve: 1. The nominal tensile strength of the bolt material is 1000MPa; 2. The yield ratio of the bolt material is 0.9; High-strength bolts, processing and manufacturing problems are compared Small, general fastener manufacturing companies can master the manufacturing process; but problems are prone to occur in material selection and heat treatment. Material selection is the primary link. Various alloying elements have a great influence on the properties of the material, and the material must be subjected to spectral composition analysis; secondly, the fracture problem and the choice of heat treatment process have a great influence and are very important. Dealers and traders must control the inspection and performance testing links; automotive fasteners have high requirements and must carefully control the quality.
We have many years of experience in the production and sales of screws, nuts, flat washers, etc. The main products are: marine lifting eye nuts, flat head countersunk head bolts, extended switch screws, B1181 hexagon nuts and other products, we can provide you with suitable fasteners for your solution Program.